以下为新加坡\韩国\深圳\美国杜邦PA66 101L尼龙66塑胶物性表：
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| DAM | 50%RH | |||||
| 基本性能 | 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 1.2 | - | % |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 8.5 | - | % | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.14 | 1.14 | --- |
| 泰伯磨耗量 | cs-17 Wheel,1000g | --- | - | 7 | mg/1000 cycles | |
| 机械性能 | 硬度计硬度 | --- | ASTM D-676 | 89 | 82 | --- |
| 洛氏硬度M | --- | ASTM D-785 | M79 | M59 | --- | |
| 洛氏硬度R | --- | ASTM D-785 | R121 | R108 | --- | |
| 拉伸强度 | 23℃ | ASTM D-638 | 82.7 | 77.2 | MPa | |
| 屈服强度 | 23℃ | --- | 82.7 | 58.6 | MPa | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 60 | ≥300 | % | |
| 屈服伸长率 | --- | ASTM D-638 | 5 | 25 | % | |
| 剪切强度 | 23℃ | ASTM D-732 | 66.2 | - | MPa | |
| 揉曲模量 | 23℃ | ASTM D-790 | 2827 | 1207 | MPa | |
| 1%形变时的压应力 | --- | ASTM D-695 | 33.8 | - | MPa | |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 53 | 112 | j/m | |
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | 504 | 1470 | KJ/m2 | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | 157 | 231 | KJ/m2 | |
| 电气性能 | 耗散因数 | 106Hz(cps) | ASTM D-150 | 0.02 | 0.1 | --- |
| 体积电阻率 | --- | ASTM D-257 | 1015 | 1013 | Ω.cm | |
| 介电常数 | 100Hz(cps) | ASTM D-150 | 4 | 8 | --- | |
| 介电常数 | 103Hz(cps) | ASTM D-150 | 3.9 | 7 | --- | |
| 介电常数 | 106Hz(cps) | ASTM D-150 | 3.6 | 4.6 | --- | |
| 耗散因数 | 100Hz(cps) | ASTM D-150 | 0.01 | 0.2 | --- | |
| 耗散因数 | 103Hz(cps) | ASTM D-150 | 0.02 | 0.2 | --- | |
| 热 性 能 | 线性热膨胀系数 | --- | ASTM D-696 | 7×10-5 | - | m/m/℃ |
| 导热系数 | --- | --- | 0.25 | - | w/mk | |
| UL可燃性导级 | --- | UL 94 | 94 | V-2 | --- | |
| 熔点 | Fisher Johns法 | ASTM D-789 | 255 | 255 | ℃ | |
| 熔点结晶 | --- | ASTM D-2177 | 270 | - | ℃ | |
| 脆化温度 | --- | ASTM D-746 | -80 | -65 | ℃ | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | 90 | - | ℃ | |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | 235 | - | ℃ | |
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | 1.4 | - | % | |
| 其它性能 | 需氧指数 | --- | ASTM D-2863 | 28 | 31 | % |